CR1100/1470QP quenched ductile steel is a high strength, high ductility steel. It is mainly composed of carbon, manganese, silicon, aluminum, vanadium and other elements. After quenching and tempering and other heat treatment processes, it has excellent mechanical properties and processing properties. This kind of steel is usually used in the field of automobile and mechanical engineering, such as body structure, engine cover, door panel and other parts, which can effectively improve the strength and safety performance of the product. Due to its excellent comprehensive properties, CR1100/1470QP quenched ductile steel has been widely used in the field of automobile and mechanical engineering.
What is the chemical composition of CR1100/1470QP quenched ductile steel?
The chemical composition of CR1100/1470QP quenched ductile steel mainly includes carbon (C), manganese (Mn), silicon (Si), aluminum (Al), vanadium (V) and other elements. The specific chemical composition is as follows:
Carbon (C): 0.08-0.13%
Manganese (Mn): 1.2-1.8%
Silicon (Si): less than 0.5%
Aluminum (Al): 0.015-0.06%
Vanadium (V): 0.1-0.2%
What are the mechanical properties of CR1100/1470QP quenched ductile steel?
The mechanical properties of CR1100/1470QP quenched ductile steel show good strength and ductility, the specific performance is as follows:
Yield strength: The yield strength of the steel is 1100-1470MPa.
Tensile strength: The tensile strength of the steel is 1300-1620MPa.
Elongation: The elongation of the steel is 8-15%.
Impact toughness: The steel has good impact toughness, generally 100-140J.
What are the applications of CR1100/1470QP in the field of automobile and mechanical engineering?
CR1100/1470QP quenched ductile steel has excellent mechanical properties such as high strength, high hardness, high toughness and high ductility, making it widely used in the fields of automobile and mechanical engineering. Here are some typical applications:
Automobile structural parts: CR1100/1470QP quenched ductile steel can be used in key components such as automobile body structural parts and airbags to improve the safety and durability of automobiles.
Mechanical structural parts: CR1100/1470QP quenched ductile steel can be used to manufacture high-strength mechanical structural parts, such as excavators, cranes, etc., to improve the bearing capacity and service life of mechanical equipment.
Rail transit equipment: CR1100/1470QP quenched ductile steel can be used to manufacture rail transit equipment, such as subway vehicles, high-speed trains, etc., to improve the safety and operating efficiency of transportation tools.
Aerospace field: CR1100/1470QP quenched ductile steel can be used to manufacture high-strength structural parts and parts in aerospace equipment, improving the durability and safety of aircraft.
What is the preparation and production process of CR1100/1470QP?
Raw material preparation: firstly, appropriate raw materials need to be selected, generally including low carbon steel, silicon, manganese, chromium and other elements. These raw materials need to be carefully proportioned and measured to ensure the accuracy and stability of the ingredients.
Steelmaking: Put the raw materials into the furnace to make steel. In the process of steelmaking, the composition and structure of the steel can meet the predetermined requirements by properly controlling the furnace temperature and adding appropriate alloying elements.
Process control: During the steelmaking process, a series of physical and chemical tests are required to ensure that the composition and structure of the steel meet the requirements. At the same time, it is necessary to control the process parameters such as heating and quenching to ensure the stable performance and quality of the steel.
Heat treatment: heat the refined steel to an appropriate temperature, and then perform quenching and tempering processes. The quenching process is to obtain high hardness and high strength of the steel through rapid cooling; the tempering process is to restore the ductility and toughness of the steel through heating and heat preservation.
Finished product processing: heat-treated steel needs to be processed, such as cutting, drilling, welding, etc., to meet the needs of different fields.
The entire production process requires a high degree of technical and process control to ensure that each step meets the requirements to guarantee the quality and performance of CR1100/1470QP quenched ductile steel.
What are the characteristics of CR1100/1470QP quenched ductile steel?
High strength and high hardness: After quenching, the steel has high hardness and high strength, which is suitable for fields requiring high-strength materials.
Good ductility and toughness: After tempering, the ductility and toughness of the steel are restored, with good plasticity and toughness, suitable for fields that require strong and tough materials.
Good cold formability: CR1100/1470QP quenched ductile steel has good machinability during cold forming, and can meet the requirements of complex parts.
Good welding performance: This steel has good welding performance and can meet the needs of different fields.
Good surface quality: CR1100/1470QP quenched ductile steel has good surface quality and finish, and is suitable for fields requiring high surface quality.
What is the heat treatment of CR1100/1470QP quenched ductile steel?
The heat treatment of CR1100/1470QP quenched ductile steel includes two processes of quenching and tempering.
Quenching treatment: heating the steel above the critical temperature, and then rapidly cooling to room temperature. This process changes the structure of the steel, giving it high hardness and strength.
Tempering treatment: reheat the quenched steel to a certain temperature, and then cool to room temperature. The process restores the ductility and toughness of the steel, increasing its plasticity and toughness.
Specifically, the heat treatment process of CR1100/1470QP quenched ductile steel is as follows:
Heating: Heating the steel above the critical temperature (usually 800-900°C) and keeping it for a certain period of time to ensure uniform heating of the steel.
Quenching: Rapidly cool the steel to room temperature. The quenching medium can be water, oil or air, etc. Different mediums have influence on the quenching effect.
Tempering: Heat the quenched steel to a certain temperature (usually 500-700°C), keep it for a certain period of time, and then cool it to room temperature.
Finished product treatment: Surface treatment such as grinding and polishing is carried out on the tempered steel to obtain the final finished product.
contact us
Our CR1100/1470QP steel products adopt the most advanced production technology and strict quality control, which ensures the high quality and stability of the products. This product has excellent mechanical properties and heat treatment properties, and can meet customers’ requirements for high strength, high hardness and high wear resistance of various parts. In addition, our CR1100/1470QP steel products also have good weldability and machinability, which is convenient for customers to carry out secondary processing and assembly.
If you are looking for high-quality CR1100/1470QP steel products and need high-quality pre-sales, sales and after-sales services, I believe that our company is your best choice. Warmly welcome you to come to consult, negotiate and cooperate!